Rubber Compounding Materials
Vulcanization Materials
Activators


309 items found
Search by for

Tradename ò
Composition
Supplier

Properties

Function & Compounding


Poly-Dispersion JZFD-90P
88% zinc oxide in a NR binder
Rhein Chemie Corporation
ï

Sp.gr. 3.50; white pellets

Vulcanizing activator for use in natural and synthetic rubber compounds.


Poly-Dispersion SR-517-50
50% Saret 517 in polymeric binder
Rhein Chemie Corporation
ï

Sp.gr. app. 1.12; encapsulated and protected form.

Crosslinkable; acrylic monomer, used in peroxide vulcanization to provide high hardness; promotes batch to batch cure rate uniformity.


Poly-Dispersion T(HRL)D-90
Fine particle size litharge in an EPDM binder
Rhein Chemie Corporation
ï

Sp.gr. 4.75; litharge 90%; very fine dispersion in elastomeric slab form, scored, dusted, and separated with PE.

chlorosulfonated polyethylene stabilizer, add in first step in mixing cycle; provides processing and handling safety, excellent dispersion, uniform cures.


Poly-Dispersion TRD-90
90% red lead oxide in an EPDM/EVA binder
Rhein Chemie Corporation
ï

Sp.gr. 4.58; orange slabs

Preferably used as an activator in acid resistant compounds. It considerably reduces the swelling of vulcanizates in water; is suitable as an oxidizing agent for the vulcanization of butyl rubber with p-quinone dioxime; can be used to improve the heat resistance in peroxide cured CPE compounds; is not recommended for use in thiadiazole cured CPE; filler in compounds for protective covering, because of the high absorption capacity to x-rays.


Polydox C-80
80% CaO in a napthenic oil binder
Polychem Dispersions
ï

Sp.gr. 2.07; calcium oxide paste dispersion

An efficient moisture absorber for all commonly used elastomers giving protection from porosity or blistering of rubber products produced in low or high-temperature cure systems.


Polydox C-90
90% CaO, oil treated
Polychem Dispersions
ï

Sp.gr. 2.43; calcium oxide, oil treated in a powder form.

Similar to Polydex C-80; is also used as a dessicant in vinyl plastisols


Polyethylene Glycol Line E-3350 plus E-200-E-20,000
Polyethylene glycol
Harwick Standard Distribution Corporation
ï

Line includes PEG-E-3350 solid along with E-4000,E-6000,E-8000 and E-20,000 sp.gr. 1.22;melt point 55-61C Semi-solid E-1450 and E-2000 sp.gr 1.13;melt point 44-48 C white powder or flake Liquids E-200 and E-400 sp.gr. 1.13

Activator used in conjunction with high surface area silicas.


Polyethylene Glycol Line E-3350 plus E-200-E-20,000
Polyethylene glycol
The Dow Chemical Company
ï

Line includes PEG-E-3350 solid along with E-4000,E-6000,E-8000 and E-20,000 sp.gr. 1.22;melt point 55-61C Semi-solid E-1450 and E-2000 sp.gr 1.13;melt point 44-48 C white powder or flake Liquids E-200 and E-400 sp.gr. 1.13

Activator used in conjunction with high surface area silicas.


Pristerene 9429
Stearic acid.
M.F. Cachat
ï

Tallow based rubber grade stearic acid; titre, 52-60°C, iodine no. 11 max., acid value 192-210 and saponification value 194-212.


Red Lead FlowSperse
90% Red Lead on different carriers
Flow Polymers LLC
ï

Past or elastomeric dispersion.

Prespersion of red lead; vulcanizer for halogenated polymers.





Red Lead Poly Slab
90% red lead in an EPR binder
Polymerics
ï

Sp.gr. 4.63; Red Lead in a rubber slab form; excellent storage stability.

Activator for NR and SRs; excellent incorporation and dispersion; very easy handling.


Rhenofit 1600
Combination of urea derivatives and dispersing agent
Rhein Chemie Corporation
ï

Sp.gr. approx. 1.25; light-colored aqueous paste

Blow promoter and deodorizer as well as vulcanization activator with built-in scorch retarder.


Rhenofit 1987
Combination of activating substances based on urea
Rhein Chemie Corporation
ï

Sp.gr. approx. 1.5; white powder.

Curing activator and promoter for reinforcing fillers


Rhenofit 2060
Magnesium oxide in a binder
Rhein Chemie Corporation
ï

Sp.gr. 3.57; light gray powder

Curing activator and acid acceptor particularly suitable for polychloroprene rubber (CR) and adhesives. a low active magnesium oxide especially selected for the use in the rubber processing industry; improves the processing safety of rubber compounds based on CR, CSM, CM and CIIR; raises the critical temperature of basic accelerators and thus prevents scorching; for acid accelerators the activating temperature is decreased; in polymers containing chlorine, especially CR, it serves as an acidacceptor and thus improves the ageing properties of the vulcanizates; in cold cured rubber coated fabrics, it is used to neutralize acid traces; moduli are generally increased by the addition of Rhenofit 2060.


Rhenofit 2120
Active magnesium oxide
Rhein Chemie Corporation
ï

Sp.gr. 3.57; white powder

An active magnesium oxide especially selected for the use in the rubber processing industry; improves the processing safety of rubber compounds based on CR, CSM, CM and CIIR; raises the critical temperature of basic accelerators and thus prevents scorching; In acid accelerators, the activiting temperature of acid accelerators is decreased; in polymers containing chlorine, especially CR, it serves as an acid acceptor and thus improves the aging properties of the vulcanizates; in cold cured rubber coated fabrics, Rhenofit 2120 is used to neutralize acid traces; moduli are generally increased by its addition.


Rhenofit 2642
Combination of activating substances based on urea bound to high activity silica
Rhein Chemie Corporation
ï

Sp.gr.. approx. 1.50; white powder, slightly hygroscopic

Accelerator activator for the vulcanization of CO and ECO.


Rhenofit CF
Specially treated very fine Ca(OH)2
Rhein Chemie Corporation
ï

Sp.gr. approx. 2.2 white powder

Crosslinking activator for fluoro-elastomers.


Rhenofit D/A
Highly reactive magnesium oxide
Rhein Chemie Corporation
ï

Sp.gr. 3.60; white powder

A highly reactive magnesium oxide intended specifically for use in the rubber processing industry; improves the processing safety of CR, CSM, CM and CIIR based rubber compounds by increasing the critical temperature of basic accelerators; reduces the susceptibility of rubber compounds to scorching; In acid accelerators, it lowers the necessary activation temperature; in polymers containing halogen, and particularly in CR, it acts as an acid acceptor, thereby improving aging properties; in cold-cured fabric proofing, it serves to neutralize traces of acid; moduli are generally increased by Rhenofit D/A.


Rhenofit EDMA/S
70% ethylene glycol dimethacrylate, 30% silica
Rhein Chemie Corporation
ï

Sp.gr. approx. 1.25; white powder, non-dusting, non-staining

Crosslinking activator for the peroxide vulcanization of synthetic rubbers.


Rhenofit F
Specially treated fine CaO
Rhein Chemie Corporation
ï

Sp.gr. approx. 3.0; white powder

Cross-linking modifier and desiccant for the use in fluoroelastomers.





Go to Page
Prev  6 7 8 9 10 11 12 13 14 15  Next
Show items at a time

Ø Main Menu
Ø Subscribe

Click companies below for more information about Activators

Suppliers listed
on this page

Rhein Chemie Corporation

Polychem Dispersions

Harwick Standard Distribution Corporation

The Dow Chemical Company

M.F. Cachat

Flow Polymers LLC

Polymerics

     