Rubber Compounding Materials
Vulcanization Materials
Activators
|
Tradename
Composition
ò
Supplier
|
Properties
|
Function
& Compounding
|
|
Mastermix MgO L 5881 Slab-40
40% low activity magnesium oxide in an FKM (genuine Viton) binder.
HEXPOL Compoundingï |
Sp. gr. 2.03.
|
Dispersed form of a low activity magnesium oxide typically used for general-purpose diamine cured FKM compounds.
|
|
Mastermix CalMag 5903 Slab-45
45% active 2:1 blend of calcium hydroxide and magnesium oxide in an FKM (genuine Viton) binder.
HEXPOL Compoundingï |
Sp. gr. 1.94.
|
A convenient dispersed blend of activators for FKM compounds.
|
|
Mastermix CalMag 5903 Slab-45
45% active 2:1 blend of calcium hydroxide and magnesium oxide in an FKM (genuine Viton) binder.
Harwick Standard Distribution Corporationï |
Sp. gr. 1.94.
|
A convenient dispersed blend of activators for FKM compounds.
|
|
Cri-FDA-45-1/1
45% disp. of codex food grade calc. hydroxide and mag. oxide in a 1/1 ratio on a fluoroelastomer base
Cri-Techï |
Sp. gr. 1.98±.05; solubility - esters and ketones; appearance - opaque, brownish, chopped or slab.
|
Used at the 10-20 part level in fluoroelastomer compounding for consistent rheology and excellent dispersion.
|
|
Cri-Act-45 1/1
45% dispersion of a 1/1 ratio of calc. hydroxide and mag. oxide on a fluorocarbon elastomer base
Cri-Techï |
Sp.gr. 1.98±.05; solubility - esters and ketones; appearance - opaque, brownish yellow, chopped or slab.
|
Used at the 10-20 part level in fluoroelastomer compounding for consistent rheology and excellent dispersion.
|
|
Cri-Act-45
45% dispersion of a 2/1 ratio of calc. hydroxide and mag. oxide on a fluorocarbon elastomer base
Cri-Techï |
Sp.gr. 1.92 ±.05; solubility - esters and ketones; appearance - opaque, brownish, chopped or slab.
|
Used at the 10-20 part level in fluoroelastomer compounding for consistent rheology and excellent dispersion.
|
|
Cri-Act-45-LV
45% dispersion of a 2/1 ratio of calc. hydroxide and mag. oxide on a fluorocarbon elastomer base
Cri-Techï |
Sp.gr. 1.96±.05; solubility - esters and ketones; appearance - opaque, brownish yellow, chopped or slab.
|
Used at the 10-20 part level in fluoroelastomer compounding for consistent rheology and excellent dispersion; for use in low viscosity compounds.
|
|
Cri-C-50
50% dispersion of calcium hydroxide on a fluorocarbon elastomer base
Cri-Techï |
Sp.gr. 1.88±.05; solubility - esters and ketones; appearance - opaque, yellow, chopped or slab.
|
Used at the 6-12 part level in fluorocarbon elastomer compounding.
|
|
Cri-Ox-50
50% dispersion of calcium oxide on a fluorocarbon elastomer base
Cri-Techï |
Sp.gr. 2.11±.05; solubility - esters and ketones; appearance - opaque, off-white, slab.
|
Used at the 4-10 part level in fluorocarbon elastomer compounding.
|
|
Mastermix HMT 400 Slab-50
50% HMT in a SBR binder
HEXPOL Compoundingï |
Sp. gr. 1.12
|
Dispersed form of HMT - Hexamethylenetetramine for use in natural and synthetic rubbers.
|
|
|
Poly-Dispersion SR-517-50
50% Saret 517 in polymeric binder
Rhein Chemie Corporationï |
Sp.gr. app. 1.12; encapsulated and protected form.
|
Crosslinkable; acrylic monomer, used in peroxide vulcanization to provide high hardness; promotes batch to batch cure rate uniformity.
|
|
Mastermix Stan-Mag MLW 4280 Paste-50
50% Stan-Mag MLW in paraffinic oil
HEXPOL Compoundingï |
Sp. gr. 1.21
|
Dispersed form of a High Activity Magnesium Oxide for use in natural and synthetic rubbers.
|
|
Drimix
50% TAC/KE
Flow Polymers LLCï |
Sp.gr. 1.56
|
Free flowing powder form of TAC in KE Clay, a coagent.
|
|
Rhenogran TAC-50
50% triallyl cyanurate in polymer binder
Rhein Chemie Corporationï |
Sp.gr. approx. 1.20, beige polymer-bound granules, problem-free dosing and mixing, excellent dispersion, fast incorporation; the bound chemical is non-dusting
|
Activator for the peroxide vulcanization of synthetic rubbers.
|
|
FE(MAG-HA)-55
55% magnesium oxide in Carnauba wax
Rhein Chemie Corporationï |
Sp.gr. 1.60; free flowing bead.
|
FE(MAG-HA)-55 dispersion is a protected form of magnesium oxide for general use in fluoroelastomer compounding; will improve dispersion, property consistency, and reduce mixing time.
|
|
DLP 1073 SR-231-55MP3
55% SR-231 on a carrier
HEXPOL Compoundingï |
Sp. gr. 1.11
|
Pelletized version of the SR-231 liquid - Diethylene glycol dimethacrylate. Easier to handle, weigh and incorporate. Carrier is LLDPE.
|
|
Mastermix Zinc Oxide 4625 Paste-55
55% Zinc Oxide in napthenic oil
HEXPOL Compoundingï |
Sp. gr. 3.06
|
Dispersed form of medium surface area zinc oxide for use in natural and synthetic rubbers.
|
|
DLP 1039 SR-350-56H
56% SR-350 on a carrier
HEXPOL Compoundingï |
|
Dry Liquid Powder - free flowing version of the SR-350 liquid - TMPTMA - Trimethylolpropane
Trimethacrylate. Easier to handle, weigh and incorporate into NR and SR compounds.
|
|
Stan-Mag DS-2 Bar
57% Magnesium Oxide
HEXPOL Compoundingï |
Sp. gr. 1.80
|
A high activity, very high surface area magnesium oxide for use as an acid acceptor in chlorinated polymers CR,CSM and CPE
|
|
Mastermix Hexa 4924 Paste-60
60% Hexa in a DOP binder
HEXPOL Compoundingï |
Sp. gr. 1.30
|
Dispersed form of HMT - Hexamethylenetetramine for use in natural and synthetic rubbers.
|
|
|
|
|